Efek suhu sintering terhadap sifat kekerasan bahan campuran Al/Cu/Sic melalui proses metalurgi serbuk

A.A.A. Triadi, I.G.N.K. Yudhyadi, I.M. Suartika, N.H. Sari

Abstract


This study aims to investigate the hardness properties of materials made of a mixture of aluminum, copper, and silicon carbide powders. The product has been made of mixtures aluminium (Al), copper (Cu) and silicon carbide (SiC) powders with a concentration of 80; 15; 5 (% wt), respectively. Manufacture of the specimens was conducted used powder metallurgy. The dimension of the specimens’ diameter of 25 mm and a thickness of 4 mm. The variation of the temperature sintering is 320, 420 and 520 oC for 40 minutes. The hardness properties have analyzed using the Brinell method. The results show that at the temperature range  320 - 420 oC, the hardness of the specimen increase to 15.2 BHN; it is due to the bond between metal powders is formed strong enough. Conversely, at 520 oC the hardness number is low because most of SiC is bound weakly to other powders. It can be concluded that the selection of temperature and sintering time and proper mixing greatly influence the hardness properties of materials yields of powder metallurgical.

Keywords


Powder metalurgy; Hardness properties; Sintering; Silicon carbida; Copper

Full Text:

PDF

References


Abbaszadeh H., 2012, Investigation on the characteristics of micro – and nano –struktured W –15 wt% Cu composite prepared by power metallurgy route, International Journal Refractory Metal Hard Materials, 30,145 –151.

Anggria F., Nawangsari P., Masnur D., 2016, Analisis pengaruh ukuran serbuk kaca pada pembuatan kampas rem sepeda motor dengan pengisi serbuk piston bekas, Jom F Teknik, 3.2.

Asghar Z., Latif M.A., Rafiuddin, Nazar Z., 2018, Effect of distribution of B4C on the mechanical behavior of Al–6601/B4C composite, Powder Metallurgy Journal, 61, 4,293–300

Brian J.W., Hoeganaes C., 2015, Powder metallurgy methods and applications, ASM Hand Book Powder Metallurgy, 7.

Cristofilini I., Molinari A., Pederzini J., Rabelli A., 2018, From experimental data, the mechanics relationships describing the behaviour of four different low alloyed steel powders during uniaxial cold compaction, Powder Metallurgy Journal, 61(1), 10–20.

Davari H.M., Gholamzadeh H., Dehghan S.H., Paydar M.H., 2017, Effect of sintering parameters (time and temperature) upon the fabrication process of organic binder–based metallic hollow sphere, Powder Metallurgy Journal, 60(5), 363–370.

Montes J.M., Cuevas F.G., Cintas J., Ternero F., Cabalero S., 2018, On the compressibility of metal powder, Powder Metallurgy Journal, 61(3), 219–230.

Mustika T.B., Sugiyono., I.N., Jujur., 2011., Pembuatan komposit AC8A/SICP dengan metode hot press metalurgi serbuk, Majalah Metalurgi, 26(3).

Sari N.H., 2018, Material teknik, Edisi pertama, Deepublish, Yogyakarta. ISBN 9786024536718.

Setiawan I., Pramono A., Irawan M.B., 2012, Analisa cacat pengaruh kompaksi proses metalurgi serbuk komposit Al/Al2O3 dari pemanfaatan limbah kaleng soft drink, Sainstek, 176–180.

Safrudin M., Yafiedan., Widyastuti., 2014, Pengaruh variasi temperatur sintering dan waktu tahan sintering terhadap densitas dan kekerasan pada MMC W–Cu melalui proses metalurgi serbuk, Jurnal Teknik Pomits, 3(1), 2337–3539.

Supriyadi S., 2017, Pengaruh ukuran serbuk logam hasil permesinan terhadap kualitas sintering magnesium AZ31 untuk aplikasi baut tulang, skripsi, Universitas Lampung.




DOI: https://doi.org/10.29303/dtm.v9i2.277

Refbacks

  • There are currently no refbacks.


Copyright (c) 2019 Dinamika Teknik Mesin: Jurnal Keilmuan dan Terapan Teknik Mesin

Creative Commons License
This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.

 
After being re-accredited, the Journal of Dinamika Teknik Mesin, still has sinta 3 (S3) which is valid until 2025.
View My Stats