Variasi persen berat tempurung kelapa terhadap konduktivitas termal komposit silicone rubber

M. Mirmanto, S. Sugiman, M.D. Ramadhani, F. Fathurrahman

Abstract


Experiments to know themal conductivities of silicone rubber composite were conducted. The sillicon rubber was mixed with coconut shells charcoal powder with weight variations. The weight presentage variations were 0, 10, 20 and 30%. Increasing the weight persentage was expected to increase the thermal conductivity of the composite. The speciment size was 50 mm x 50 mm x 5 mm. The speciments were tested according to the conduction heat transfer mode. To make sure that the temperatures were steady, the experiments were performed for about 6 hours. The results indicated that increasing the weight presentage raised the composite thermalconductivities. At 0% of wight, the composite had a thermalconductivity of 0.157 W/m°C, at 10%, 20% and 30% of weight compositions; the composite had thermal conductivities of 0.461 W/m°C, 0.58 W/m°C, and 0.73 W/m°C respectively.


Keywords


right presentage; Silicon rubber; Coconut shells charcoal powder; Thermal conductivity

Full Text:

PDF

References


Ardhyananta H., Pakaya F., Wicaksono S.T., 2016, Rasio swel dan ketahanan kimia dari blend epoksi/ poli (amino amida)/vtk karet silikon, Prosiding Seminar Nasional Kulit, Karet dan Plastik Ke-5, Yogyakarta, 26 Oktober.

Asrori M.Z., 1997, Analisis kestabilan panas polianilin dan karakterisasinya sebagai material polimer konduktif, Tesis, Depok FMIPA UI.

Callister Jr. W.D., Rethwisch D.G., 2018, Fundamentals of material science and engineering: An integrated approach, 5th Edition, John Wiley and Sons Inc, Usa.

Cengel Y.A., Ghajar A.J., 2015, Heat and mass transfer, Penerbit McGraw-Hill Education, New York.

Direktorat Jendral Perkebunan, 2012, Statistik perkebunan indonesia kelapa sawit (oil palm) Jakarta 2010-2012.

Holman, J.P., 2002, Heat Transfer, McGraw-Hill Education (India) Pvt Limited.

Incropera, F., DeWitt, D.P., Bergman, T.L. Lavine, A.S., 2006, Fundamentals of Heat and Mass Transfer, 6th Edition, John Wiley & Sons, Hoboken.

Purwono A.H., Priyanto K., Pangestu K.S.A., 2019, Studi konduktivitas termal komposit geopolimer dengan matriks hdpe daur ulang sebagai bahan interior door trim kendaraan, Teknika , 6(2), 40-44.

Sijabat F.I., Saragih J., Halimatuddahliana, 2013, Pengaruh ukuran serbuk tempurung kelapa sebagai pengisi komposit poliester tak jenuh terhadap sifat mekanik dan penyerapan air, Jurnal Teknik Kimia USU, 2(4).

Sujana W., Widi I.K.A., 2013, Pemanfaatan silicon rubber untuk meningkatkan ketanggihan produk otomotif buatan lokal, Jurnal Energi dan Manufaktur, 6 (1), 37-42.

Vidia R., 2019, Pengujian konduktivitas termal komposit bermatriks polyester dan vinyl ester dengan penguat serat nata de coco, Skripsi, Jurusan Teknik Mesin Fakultas Teknik Universitas Andalas Padang.




DOI: https://doi.org/10.29303/dtm.v11i2.450

Refbacks

  • There are currently no refbacks.


Copyright (c) 2021 M. Mirmanto, S. Sugiman, M.D. Ramadhani, F. Fathurrahman

Creative Commons License
This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.