BENDING AFTER IMPACTKOMPOSIT SANDWICH BERPENGUAT SERAT BAMBU-FIBERGLASS DENGAN COREPOLYURETHANE RIGID FOAM

Agus Dwi Catur, S. Sinarep, Paryanto Dwi Setyawan, Achmad Zainuri, S. Supriadi

Abstract


Impact of the composite sandwich made of materials that become defect, how defects after impact  in material need to be examined .Is that defected composites and wich still has the strength toremain in use?, then the bending after impact strength testing must be done to answer these questions.Composite sandwich with bamboo fiber-fiber glass reinforcement and with a core of 25mm rigid polyurethane foam sheet was produced. Composite sandwich made with two composite sandwich laminate as skinflanking the core. Laminated composite sandwich in this study varied number of layers of reinforcing fibers and type of fiber. Specimens subjected to drop weight impact with varying energy then defect researched and bending  after impact strengthtested.
Defects formed on the composite experiencing a drop weight impact loads are: delamination, basin and through hole. The more layers of reinforcing fibers in the composite skin causing moreshallowbasinformed by theresidualimpact. The greater the impact energy causes greater depth of residual basin. Composite sandwich still has the bending strength after impact. Residual bending strength decreases with increasing impact energy imposed on the composite.

Full Text:

PDF

References


Labor(2005), United States Department of Occupational Safety & Health Administration, Chemical Sampling Information, CAS Registry Number: 65997-17-3 (Fibrous Glass).

Shukla, K. S., and Janardhan Prasad. "Reconstituted wood from bamboo for structural uses." Journal of the Indian Academy of Wood Science,volume19, issue 1 (1988): 19-27.

Shukla, N.K.; Singh, R.S.; Sanyal, S.N, "Strength properties of eleven bamboo species and study of some factors affecting strength" of the Indian Academy of Wood Science, ISSN: 0379-5497, volume19, issue 2 (1988): 63-80.

Xiaobo Li, 2004, Physical, Chemical, and Mechanical Properties of Bamboo and Its Utilization Potential for Fiberboard Manufacturing, A Thesis,Graduate Faulty of the Louisiana State University and Agriculture and Mechanical College.

Bansal, Arun K. Zoolagud, S.S., Bamboo composites: Material of the future, Journal of Bamboo and Rattan, Volume 1, Number 2, 2002 , pp. 119-130(12).

Zhou, G,2009,Impact Damage and Energy-absorbing Characteristics and Residual In-plane Compressive Strength of Honeycomb Sandwich Panels, Journal of Sandwich. Structures and Materials; 11; 329.

I. M. De Rosa, F. Marra, G. Pulci, C. Santulli, F. Sarasini, J. Tirillò, M. Valente,2011,Post-impact mechanical characterisation of E-glass/basalt woven fabric interply hybrid laminates, eXPRESS Polymer Letters Vol.5, No.5 (2011) 449–459.

Mehmet Aktas, H. Ersen Balcıog˘lu, Alaattin Aktas, Erkan Turker, M. Emin Deniz,2012,Impact and post impact behavior of layer fabric composites, Composite Structures, 94, 2809–2818.


Refbacks

  • There are currently no refbacks.


Copyright (c) 2017 Dinamika Teknik Mesin

Creative Commons License
This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.