ANALISIS SIFAT KEKUATAN TARIK DAN KEKUATAN BENDING KOMPOSIT HIBRYD SERAT LIDAH MERTUA DAN KARUNG GONI DENGAN FILLER ABU SEKAM PADI 5% BERMATRIK EPOXY

Jauhari Muslim, Nasmi Herlina Sari, Emmy Dyah Sulistyowati

Abstract


Abstract

The use of composite materials is growing at over the development of manufacturing industry. Composites sansevieria and hibiscus canabinus with the addition of rice husk ash filler. The purpose of this study was to analyze the tensile strength and bending strength of hybrid composites sansevieria and hybiscus canabinus with rice husk ash filler epoxy bermatrik with random fiber direction.

Variation of fiber volume fraction sansevieria and hybicus canabinus is 0%:35%,10%:25%, 15%:10%, 20%:15%, 25%:10%, 35%:0%. Method for making composite specimens in the form of hand lay up with a fiber length of 2cm. Testing was done by bending test following the ASTM standard D790 tensile test and ASTM D3039 standards.

The results showed that the composites with rice husk ash fillers higher bending strength and the strength of its appeal compared to the composite without using rice husk ash fillers, where the highest bending strength on volume fraction 0%/35% as big as 32,00 MPa (using filler), and kekutan lowest bending the volume fraction 0%/35% as big as 21, 69 Mpa (without filler). While the tensile test has the highest power in the volume fraction 15%/20% as big as 8,24 MPa (using filler), and the lowest tensile strength on volume fraction 0%/35%  as big as 3,43 MPa (without filler).


Full Text:

PDF

References


Bismarck, A., Askargorta, I.A., Lamphe, T., Wielaye, B., Stamboulis, A., Skenderovich, I., Limbach, H.H., 2006, Surface Characterization of Flax, Hemp and Cellulose Fibres: Surface Properties and the Water Uptake Behavior, Polymer Composite Vol 23, no. 5.

Budinski, Kenneth., 2000, Engineering Materials Properties and Selection sixth Edition, Prentice Hall, New Jersey.

Dharma Putra,2006. Jurnal ilmiah teknik sipil vol 10, no 2, Universitas udayana

Diharjo, K., 2005, Pengaruh Perlakuan Alkali terhadap Sifat Tarik Bahan Komposit Serat Rami-Polyester, Jurnal Teknik Mesin Fakultas Teknik Universitas Negeri Sebelas Maret, Surakarta

Febrianto, 2004, Menyelidiki kekuatan bending dan impak komposit hibrid sandwich kombinasi serat karung Goni dan serat Gelas-polyester dengan core kayu Sengon Laut (Albizzia Falcata).

Feldman. D., dan Hatomo, J.A., 1995, Bahan Polimer Konstruksi Bangunan, Gramedia Pustaka Utama.

Gibson, F.R., 1994, Principle of Composite Material Mechanis, International Edition, McGraw-Hill Inc, New York.

Hadi, 2000, Mekanika Struktur Komposit, Direktoral P3M Dirjen Dikti Depdiknas, Jakarta.

Hartomo,A.J., Rusdiarsono, A., Hardianto, D., 1992, Memahami Polimer dan Perekat, Andi Offset. Yogyakarta.

Ismoyo, 1994, Karakteristik kekuatan bending komposit berpenguat kombinasi serat kenaf acak dan anyam. Universitas Muhamadiah, Malang.

Justus Sakti Raya., 2001, Technical Data Sheet, Jakarta.

Khanam,2007, Tensile, Flexural and Compressive Properties of Sisal/Silk Hybrid Composites, Journal of Reinforced Plastics and Composites, 1065-1069

Khoatane, M. C2008. Hemp Fiber-Reinforced Pentene/Polypropylene Copolymer: The Effect of Fiber Loading on the Mechanical and Thermal Characteristics of the Composites, Journal of Reinforced Plastics and Composites,vol.27,hal. 1533.

Lokantara, P., dan Suardana, N.P.G., 2007, Analisis Dan Perlakuan Serat Tapis Serta Rasio Epoxy Hardener Terhadap Sifat Fisis Dan Mekanis Komposit Tapis/Epoxy, Jurnal Ilmiah Teknik Mesin CAKRAM Vol.1 No.1, Universitas Udayana, Bali

Murray, 1999, Terobosan baru memperkecil kandungan karbondioksida di udara menggunakan stek daun lidah mertua. Universitas Muhamadiah, Malang.

Mohammad Romi (2003), Tugas Akhir Jurusan Teknik Mesin, Universitas Mataram.

Profesor Jamasri, Tim reviewer monitoring dan evaluasi PKM 2012, Yogyakarta.

Purwanto (2006) ,Tugas Akhir Jurusan Teknik Mesin, Universitas Mataram.

Richardson, J. T. E., Eysenck, M. W., and Warren Piper, D. (eds) (1987). Student Learning: Research in Education and Cognitive Psychology. Milton Keynes: SRHE & Open University Press.

Rizvi F. B., Rashed., 2006, Effects Of Process Parameters On Tensile Strength Of Jute Fiber Reinforced Thermoplastic Composites,Department of Materials and Metallurgical Engineering, Bangladesh University of Engineering and Technology, Dhaka -1000, Bangladesh. Journal of Naval Architecture and Marine Engineering Juni, 2006

Sabari, Is., 2009, Pengaruh Fraksi Volume Serat Terhadap Kekuatan Tarik, Harga Impak Dan Kemampuan Serapan Bunyi Dari Komposit Serat Sabut Kelapa Anyaman 3D, Tugas Akhir, Universitas Muhammadiyah Surakarta

Satish, K. G., Siddeswarappa, B., Mohamed Kaleemulla, K., 2010, Characterization of In-Plane Mechanical Properties of Laminated Hybrid Composites., Journal of Minerals & Materials Characterization & Engineering., Department of Mechanical Engineering, University B.D.T. College of Engineering and Davangere Department of Industrial and Production Engineering, University B.D.T. College of Engineering, Davangere 577004, India.

Schwartz, M.M., 1984, Composite Materials Handbook, McGraw-Hill Book Co., New York.

Siriwardena, S., Ismail, H., Ishiaku, U.S. 2003, A Comparison of the Mechanical Properties and Water Absorption Behavior of White Rice Husk Ash and Silica Filled Polypropylen Composites, Journal of Reinforced Plastics and Composites, vol. 22, hal.1645.

Sulistijono., 2008, Analisa Pengaruh Fraksi Volume Serat Kelapa Pada Komposit Matriks Polyester Terhadap Kekuatan Tarik, Impact Dan Bending, Tugas Akhir, ITS, Surabaya.

Supardi, 1999, Pengujian Logam, Angkasa Bandung, Bandung.

Tata sudira, dan Shinroku saito, 1985, Pengetahuan bahan teknik. PT. Prandnya Diaramita, Jakarta.


Refbacks

  • There are currently no refbacks.


Copyright (c) 2017 Dinamika Teknik Mesin

Creative Commons License
This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.