Pengaruh variasi campuran serbuk kayu jati (tectona grandis l.) dan sekam padi pada pembuatan material komposit kampas rem

R.F. Lubis; L.H. Pasaribu; M.I. Nasution

doi:10.29303/dtm.v14i1.783

Pengaruh variasi campuran serbuk kayu jati (tectona grandis l.) dan sekam padi pada pembuatan material komposit kampas rem

R.F. Lubis, L.H. Pasaribu, M.I. Nasution

Abstract

Brake pad composite materials are made from organic materials and are harmless to the environment. In this study, the brake pad composite material was made using teak wood powder, rice husk and aluminium. Comparison of variations A (23.5 grams of teak wood powder, 18.5 grams of rice husk and 7 grams of aluminium powder) B (27 grams of teak wood powder, 15 grams of rice husk and 7 grams of aluminium powder) C (30.5 grams of teak wood powder, 11.5 grams of rice husk and 7 grams of aluminium powder) and the addition of 21 grams of polyurethane resin then compressed for 30 minutes at 100 ⁰C for 20 minutes. The test results of density, hardness, flexibility and wear were compared with SAE J661. Based on the test results, it was found that samples A, B and C met the SAEJ661 standard only in the flexure test with a value of 490.33 - 529.55 N/cm². Teak wood powder can increase the value of flexibility while rice husk is used to increase the value of density, hardness and wear due to its silica content.

Keywords

Break pad; Teak wood; Rice husk

Full Text:

PDF

References

Bagaskara, A., Widodo, S., Pramono, C., Pengaruh serbuk kulit biji mangga sebagai penguat komposit kampas rem terhadap sifat mekanis, Jurnal Teknik Mesin, 9(1), 1-7, 2020.

Desiasni, R., Widyawati, F., Monica, R., Pengaruh ukuran partikel terhadap sifat fisika dan mekanik komposit limbah limbah gergaji kayu jati dengan matrik resin epoxy, Jurnal Teknik dan Sains, 3(1), 46-52, 2022.

Dwi Handoko, R., Setiawan, F., Sehono, Pengaruh fraksi serbuk kayu jati terhadap kekuatan komposit partikel dengan pengujian impact, Jurnal Teknik, Elektronik, Engine, 8(2), 322–329, 2022.

Ginting S, E., Putri, I, S., Puspitasari, R., Arsela, R., Firdaus, I., Sembiring, S, karakteristik struktur mikro dan gugus fungsi komposit silika sekam padi dan aspal, Jurnal Teori dan Aplikasi Fisika, 8(1), 93-100, 2020.

Gugun, G., Alamsyah, M, H, Analysis of mechanical properties character of mechanics composite brake pads material reinforced by teak wood powder and brass powder, Jurnal Rekayasa Energi Manufaktur, 5(1), 9-12, 2020

Gunadi, W, Prospek dan strategi bersaing pada industri furniture berbahan kayu jati, Jurnal Ilmiah M-Progres, 11(1), 1-15, 2021

Haroen, W. K., Rekayas mesin pencetak kampas rem serat pulp non-asbestos. Jurnal Simetris, 8(1), 1-7, 2017.

Ihsan, N.M., Wicaksono, D., Sehono, S, Uji keausan kampas rem berbahan limbah organik menggunakan metode ogoshi. Teknika STTKD: Jurnal Teknik, Elektronik, Engine, 8(1), 92–96, 2022

Kosjoko, K., Mufarida, N. A, Pemanfaatan limbah serbuk arang kayu jati (tectona grandis l.f) sebagai material brake pads. j-proteksion: Jurnal Kajian Ilmiah dan Teknologi Teknik Mesin, 7(1), 21–27. 2022.

Kristianta, F., Kristian T, A, I., Sholahuddin, I, Variasi ukuran terhadap kekerasan dan laju keausan komposit epoxy aluminium-serbuk tempurung kelapa untuk kampas, Jurnal Rekayasa Mesin, 8(3), 149–153. 2017.

Kurniawan, M.A., Prasetiyo, Y., Srianto, S., Fahmadi, A.E., Rifano, R., Characterization of brake pads by variation in composition of teak wood powder and rice husk ash, RSF Conference Series: Engineering and Technology, 2(2), 190–197, 2022.

Laksono, A.D., Ernawati, L., Maryant, D., Pengaruh fraksi volume komposit polyester berpenguat limbah sebuk kayu bangkirai terhadap sifat material akustik, Jurnal Rekayasa Mesin, 10(3), 277-285, 2019.

Lazuardi, M., Hartono, M., Pengaruh komposisi dan temperatur material biokomposit terhadap kinerja kampas rem non asbestos, Jurnal Energi dan Teknologi Manufaktur, 05(01), 29–34., 2022

Mubarrok, M.H., Pengaruh ukuran serbuk kuningan terhadap ketahanan aus, koefisien gesek dan kekerasan kampas rem, Penerbit Fakultas Teknik Universitas Muhammadiyah Surakarta, Surakarta, 2014.

Purboputro, P.I, Pembuatan kampas rem menggunakan serat pelepah pisang dengan variasi butiran aluminium silikon (Al-Si) mesh 50, 60, 100 terhadap tingkat kekerasan, keasusan, dan koefisien gesek, Simposim Nasional RAPI XX, 223-228, 2021.

Septiyanto, A,R., Suroso, I., Utami, N, Analisis kekerasan dan keausan bearing pada pesawat cessna grand carravan 208B. Turbo, 11(1), 117–124, 2022

Sidiq, M.F., Optimlasisasi suhu sintering terhadap sifat mekanis komposit serbuk kayu jati, serbuk tempurung kelapa dan kuningan dengan resin epoxy pada kampas rem, Penerbit Fakultas Teknik Universita Tidar, Magelang, 2022

Sukamto, Mulyanti, J., Swandono, A., Kekuatan lengkung dan impak material parket lantai berbahan dasar serbuk gergaji kayu jati, Seminar Nasional Diseminasi Hasil Penelitian 2021 Universitas Janabadra Yogyakarta, 326-330, 2021.

DOI: https://doi.org/10.29303/dtm.v14i1.783