PENGARUH PREHEAT DAN TEMPERING TERHADAP KEKERASAN DAN STRUKTUR MIKRO HASIL PENGELASAN BAJA JIS SS 400

Saiful Askar, S. Sinarep, Nasmi Herlina Sari

Abstract


JIS steel SS 400 is one of the most common types of steel used for hot rolling steel structures general. This steel is excellented to the weldability and machinability properties. This study aimed to determine the effect of heat treatment with preheating without tempering (PTT), with preheating and tempering (PT), without preheating and without tempering (TPTT), and  without preheating tempering (TPT). The test results are then compared with the raw material specimens.

Method of forming specimens using welding SMAW (Shielded Metal Arc Welding) DC reverse polarity using E7018 type electrode diameter of 4 mm. Type of seam used is V open seam with slit width and height of 2 mm and the width of the root angle 70o. This studied used a low alloy steel (JIS steel SS 400) which contain high levels of 0.20% C, maximum 0.005% S, maximum 0.005% P with repetitions each variation three times. Tests conducted it has testing the tensile strength, brinell hardness testing, and microstructure photo shoot.

Value of the brinell hardness of welded joints highest in the tempering specimens without preheating, amounting with  163,911 HB hardness value. The structure of cementite and pearlite formed. While the lowest hardness values of specimens owned by raw material is 120,498 HB hardness values that form the microstructure of pearlite and ferrite. 


Full Text:

PDF

References


Callister, 2000, Hand’s Book Fundamental of Material Science and Engineering 5th Edition, Department of Metallurgy Engineering, The University of Utah.

Copyright© ASM International® 1995

Dieter, 1976, Metallurgy SI Metric Edition Mechanical, University of Mariland

http://www.meadinfo.org/ diakses tanggal 09 Desember 2011 Jam 23.50WITA.

http://www.migas-indonesia.Com/ diakses tanggal 29 Desember 2011 Jam 16.34WITA.

Kurniawan, Apri, 2011, Jenis-jenis Pengelasan, Jurusan Pendidikan Teknik Mesin, Fakultas Teknik, Universitas Negeri Yogyakarta

Loureiro, Altino J.R., 2000, Effect of Heat Input on Plastic Deformation of Undermatched Welds, Department of Mechanical Engineering, University of Coimbra, Pinhal de Marrocos, 3030 Coimbra, Portugal.

Santoso, Joko, 2006, Pengaruh Arus Pengelasan terhadap Kekuatan Tarik dan Ketangguhan Las SMAW dengan Elektroda E7018, Jurusan Teknik Mesin, Fakultas Teknik, Universitas Negeri Semarang, Semarang.

Vlack, Lawrence H. Van, 2004, Elemen-elemen Ilmu dan Rekayasa Material, Edisi Enam, Erlangga, Jakarta.

Wiryosumarto, Harsono & Okumura, Toshie, 2004, Teknologi Pengelasan Logam, Cetakan 9, Pradnya Paramita, Jakarta.

Yaqin, Muhammad Khusnul, dkk., 2011, Pengaruh Preheat dan Postheat terhadap Lebar HAZ, Struktur Mikro, dan Distribusi Kekerasan pada Proses Pengelasan SMAW Besi Cor Kelabu FC 25, Jurusan Teknik Material dan Metalurgi, Institut Teknologi Sepuluh November, Surabaya.

Yosga, Muchamad, 2012, Diagram TTT (Time-Temperature-Transformation), Universitas Brawijaya.

Zamrinata, 2011, Tujuan dan Jenis Perlakuan Panas, Program Studi Teknik Mesin, FKIP, UNS.


Refbacks

  • There are currently no refbacks.


Copyright (c) 2017 Dinamika Teknik Mesin

Creative Commons License
This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.

 
After being re-accredited, the Journal of Dinamika Teknik Mesin, still has sinta 3 (S3) which is valid until 2025.
View My Stats